Solef 6008 by Syensqo is a low molecular weight, low-viscosity polyvinylidene fluoride homopolymer. It is a semi-crystalline and additive-free grade. It is suitable for processing by injection molding. It has the intrinsic stability inherent to fluoropolymers even when exposed to harsh thermal, chemical and UV environments.

Technical data sheet

Physical

Property	Typical Value	Unit	Test Method
Density / Specific Gravity	1.75 to 1.80	-	ASTM D792
Melt Mass-Flow Rate (MFR)			ASTM D1238
230°C/2.16 Kg	5.5 to 11 g/10 min
230°C/5.0 Kg	16 to 30 g/10 min
Molding Shrinkage - Flow	2.0 to 3.0 %	-
Water Absorption (24 hr, 23°C)	< 0.040 %	-	ASTM D570

Mechanical

Property	Typical Value	Unit	Test Method
Tensile Modulus (23°C, 2.00 mm)	1800 to 2500 MPa	-	ASTM D638
Tensile Strength
Yield, 23°C, 2.00 mm	50.0 to 60.0 MPa		ASTM D638
Break, 23°C, 2.00 mm	30.0 to 50.0 MPa		ASTM D638
Tensile Elongation
Yield, 23°C, 2.00 mm	5.0 to 10 %		ASTM D638
Break, 23°C, 2.00 mm	200 to 300 %		ASTM D638
Coefficient of Friction			ASTM D1894
vs. Itself - Dynamic	0.15 to 0.35
vs. Itself - Static	0.20 to 0.40
Taber Abrasion Resistance			ASTM D4060
1000 Cycles, 1000g, CS-10 Wheel	5.0 to 10.0	mg
Impact
Charpy Notched Impact Strength^1			ASTM D6110
23°C, 4.00 mm	40.0 to 120	J/m
Hardness
Durometer Hardness (Shore D, 1 sec, 2.00 mm)	73 to 80		ASTM D2240

Table 3: Solef® 6008 PVDF - Thermal Properties

Property	Typical Value	Test Method
Glass Transition Temperature	-40 °C	ASTM D4065
Vicat Softening Temperature	135 to 145 °C	ASTM D1525
Melting Temperature	170 to 175 °C	ASTM D3418
Peak Crystallization Temperature (DSC)	134 to 144 °C	ASTM D3418
CLTE - Flow (10 to 40°C)	14-4 cm/cm/°C	ASTM E968
Specific Heat	1200 J/kg/°C (23°C), 1800 J/kg/°C (100°C)	-
Thermal Conductivity (23°C)	0.20 W/mK	ASTM C177
Crystallization Heat	54.0 to 60.0 J/g	ASTM D3417
Heat of Fusion	58.0 to 67.0 J/g	ASTM D3417

Table 4: Solef® 6008 PVDF - Electrical Properties

Property	Typical Value	Test Method
Surface Resistivity	> 10^14 ohms/cm	ASTM D257
Volume Resistivity	> 10^14 ohms-cm	ASTM D257
Dielectric Strength (23°C, 1.00 mm)	20 to 25 kV/mm	ASTM D149
Dielectric Constant (23°C, 1 kHz)	7.00 to 10.0	ASTM D150

Flammability

Property	Typical Value	Unit	Test Method
Flame Rating (2.00 mm)	V-0	UL 94	-
Oxygen Index (3.00 mm)	44 %	ASTM D2863	-

Product Functions

Low VOC
High Purity
High ESCR (Stress Crack Resist.)
Sour Gas Resistant
Acid Resistant
Mineral/Synthetic Oil Resistant
Detergent Resistant
Hydrolysis Resistant
Low Moisture Absorption
Piezoelectric Properties
Flame Retardant
Fatigue Resistant
High Hardness
High Stiffness
Creep Resistant
Good Impact Resistant
Low CLTE
UV Resistant
Radiation (Gamma) Resistant
Good Processing Stability
Autoclave Sterilizable (steam)
E-beam Sterilizable
Radiation Sterilizable
Ethylene Oxide Sterilizable
Heat Sterilizable
Good Thermal Stability
High Heat Resistant

Applications of Solef 6008/0001

Industrial applications

Segments	Applications
Industrial Equipment	Industrial Equipment Parts